TX-2188 adhesive

TX-2188 adhesive is a two-component (A/B) acrylate copolymer emulsion adhesive, mainly is suitable for the active carbon powder solid particles forming. The A/B component has independence groups after curing crosslinking reaction, excellent waterproof, acid proof, alkali resistant function, so as to improve the adsorption material of granular in acid, alkali system service life, save cost, improve efficiency.

One, the main technical indexes:

(1): A appearance of components of the milky white sticky liquid; group B: dark brown viscous liquid.

(2) solid content: A group (S=48 ± 2%); B group (S=99 ± 1%).

The pH value (3): A group (5 ~ 7).

(4) viscosity: A component (8000 ~ 12000mpas); group B (2000 ~ 5000mpas).

Two, application: widely used in active carbon powder solid particles forming.

Characteristics: (1) the A/B component according to the proportion of (1:10 ~ 20%) after curing, good

And pressure performance, prolong the particle adsorption material can be reused time.

(2) with good water resistance, acid resistance, alkali resistance, improve the adsorption material

(3) the A/B component according to the proportion of resin formed after curing is non-toxic materials.

Four, application method and the matters needing attention:

(1) the component A:B = 1:10 ~ 20% mixed evenly, can be added according to the actual need

A certain proportion of water and stir well.

(2) the active carbon powder in certain proportion and above (A / B) and the amount of mixed gum

The water in a mixing machine mixing, pelletizing, drying and shaping.

(3) the use of glue before the first component A uniform mixing, stirring and adding component B, until smooth.

The mixed glue 1 ~ 2 hours applicable period, which must be used up in the application period, otherwise

After cannot use.

(4) A / B component glue after use must be more than the rubber seal (especially the B component to curing

Scrap).

(5) must not be mixed with other glue glue, so as not to affect the quality and use effect.