TX-2188 (Ⅱ) water purification filter material setting adhesive is a two-component (A/C) acrylate copolymer lotion adhesive, which is mainly suitable for forming spherical or columnar solids of various powder adsorption materials (such as diatomite, natural mineral soil, etc.). There are unique functional groups between the A/C components that undergo crosslinking reactions, resulting in high hardness and good water resistance after curing. Using less glue, reducing pore blockage, and having excellent adsorption performance.

1,Main technical indicators:

(1) Appearance: Component A - milky white viscous liquid; C component - dark brown viscous liquid.

(2) Solid content: Component A (S=31 ± 1%); C component (S=99 ± 1%).

(3) PH value: Component A (5.0~7.0).

(4) Viscosity: Component A (35000-4500mpa.s)/250C; C component (200-400mpa.s)/250C.

2,Applicability: Widely used for various powdered adsorption materials (such as diatomaceous earth, natural mineral soil, etc.) to form spherical or columnar solids.

3,Characteristics:

(1) After the A/C component is cured in proportion (100:5-10%), it has good fastness and pressure resistance, as well as good hardness.

(2) It has good water resistance, less adhesive usage, reduces pore blockage, and excellent adsorption performance.

(3) The resin formed after the A/C component is cured in proportion is a non-toxic material.

4,Applicable methods and precautions:

(1) Mix the components (A: C=100:5-10%) evenly (you can add water in appropriate proportions and stir well according to actual needs).

(2) Mix the powdered solid in a certain proportion with the above mixed adhesive (100:150-180) in a mixer, and then granulate (using different equipment to make columns or balls as needed). Dry at 1300C for 3 hours to form, and then air dry naturally for 24 hours.

(3) Before using the glue, mix component A evenly, add component C while stirring, and then add an appropriate amount of water until uniform. This mixed adhesive has a shelf life of 1-2 hours, which means it must be used up within the shelf life, otherwise it cannot be used after curing.

(4) After using the adhesive components A and C, the remaining adhesive must be sealed properly (especially when component C is prone to solidification and is scrapped).

(5) Do not mix with other adhesives to avoid affecting the quality and effectiveness of the adhesive.

(6) This product should be stored in a dry and cool place, with a suitable storage and use temperature of 5-300C, avoiding direct sunlight.

5,Packaging specifications: TX-2188 (II) A/50Kg, TX-2188 (II) C/25Kg, 200Kg plastic drum. Transport ordinary goods.

Note: The technical information of this product is obtained based on theory and years of experience of our company, but does not serve as a guarantee of responsibility. Customers should first request samples and choose to use them themselves before use. If you encounter any difficult problems during production, you can contact our technical department, and we will fully cooperate to meet the customer's requirements.